MULTIFUNCTIONAL FIBERS BASED ON POLYAMIDE 6 AND PLASMA FUNCTIONALIZED CARBON NANOTUBES MoDeSt 2012 Conference, Praga, 2-6 Settembre 2012.
2012
Commercial (CNT 1) and ad hoc synthesized carbon nanotubes (CNT 2) were plasma treated under oxygen atmosphere and then added to polyamide 6 (PA 6) in order to prepare multifunctional fibres by melt spinning. For comparison, pristine nanofillers were used too. The effect of functionalization and of filler characteristics on the morphological, rheological, mechanical and electrical properties of the fibers was studied by TEM and SEM, rheological measurements, tensile tests and electrical conductivity tests. The amalysis of Raman spectra put into evidence that the intensity of D-band (correlated with the degree of functionalization by the different vibration mode of carbon atoms in the presen…
Comportamento di nanocompositi PA6/CNT in flusso elongazionale non isotermo
2012
Si sono preparate fibre a matrice poliammidica caricate con CNT. Sono state utilizzate due diverse tipologie di CNT a differente fattore di forma e grado di purezza, ossidate mediante plasma di ossigeno. Le misure di viscosità elongazionale hanno evidenziato che l’introduzione della carica comporta un incremento della MS a fronte di una diminuzione della BSR per tutti i materiali caricati. La tipologia e la funzionalizzazione dei CNT hanno delle notevoli ricadute sul diverso comportamento reologico. Studi morfologici hanno evidenziato che dopo la funzionalizzazione si registrano livelli di dispersione, allineamento e adesione interfacciale più alti. La natura delle interazioni matrice-caric…